Yttria stabilized tetragonal zirconia ceramics: preparation, characterization and applicationspplications

Authors

  • N Sultana Department of Applied Chemistry and Chemical Engineering, Noakhali Science and Technology University, Sonapur, Noakhali
  • K Bilkis Department of Applied Chemistry and Chemical Engineering, Noakhali Science and Technology University, Sonapur, Noakhali
  • R Azad Department of Applied Chemistry and Chemical Engineering, Noakhali Science and Technology University, Sonapur, Noakhali
  • MR Qadir Pilot Plant and Process Development Centre (PP & PDC), BCSIR, Dhaka-1205
  • MA Gafur Pilot Plant and Process Development Centre (PP & PDC), BCSIR, Dhaka-1205
  • MZ Alam Department of Applied Chemistry and Chemical Engineering, University of Dhaka, Dhaka 1000

DOI:

https://doi.org/10.3329/bjsir.v53i2.36671

Keywords:

Yttria stabilized tetragonal zirconia (YSTZ), Zirconia, Tetragonality, Optical ferrule

Abstract

In this study, yttria stabilized tetragonal zirconia (YSTZ) ceramics were prepared and were sintered at different temperatures to find out the optimum sintering temperature for their better tetragonality and mechanical properties for their application as optical ferrule. Vicker’s hardness was performed by micro hardness tester and it was found to increase with the increase of sintering temperature to a maximum value, then it was decreased with higher sintering temperature. Water absorptivity and porosity were also seen to decrease as the densities of the specimens were increased. X-ray diffraction was employed to determine crystal structure of sintered samples. Surface morphology of the sintered samples was examined through field emission scanning electron microscope.

Bangladesh J. Sci. Ind. Res.53(2), 111-116, 2018

Downloads

Download data is not yet available.
Abstract
64
PDF
18

Author Biography

N Sultana, Department of Applied Chemistry and Chemical Engineering, Noakhali Science and Technology University, Sonapur, Noakhali



Downloads

Published

2018-05-27

How to Cite

Sultana, N., Bilkis, K., Azad, R., Qadir, M., Gafur, M., & Alam, M. (2018). Yttria stabilized tetragonal zirconia ceramics: preparation, characterization and applicationspplications. Bangladesh Journal of Scientific and Industrial Research, 53(2), 111–116. https://doi.org/10.3329/bjsir.v53i2.36671

Issue

Vol. 53 No. 2 (2018)

Section

Articles

License

Bangladesh Council of Scientific and Industrial Research (BCSIR) holds the copyright to all contents published in Bangladesh Journal of Scientific and Industrial Research (BJSIR). A copyright transfer form should be signed by the author(s) and be returned to BJSIR.

The entire contents of the BJSIR are protected under Bangladesh Council of Scientific and Industrial Research (BCSIR) copyrights.

Creative Commons Licence
BJSIR is an open access journal, and articles are distributed under the terms of the Creative Commons Attribution-NonCommercial License (CC BY-NC) Creative Commons Attribution-NonCommercial 4.0 International License which allows others remix, tweak, and build upon the articles non-commercially, and although their new works must also acknowledge and be non-commercial, they don’t have to license their derivative works on the same terms.