Effect of Ca-substitution on the Magnetic and Dielectric Properties of Mn-Zn Ferrites

Abstract

Spinel Mn-Zn ferrites with composition Mn_xZn_0.4Ca_0.6-2xFe_2+xO₄, where x = 0.10, 0.15, 0.20, 0.25 and 0.30 have been prepared by conventional ceramic technique sintered at    1300 °C for 4 hours. The influence of Ca-substitution on various properties of Mn-Zn ferrites have been studied in this work. Investigations were carried out by the measurements of Curie temperature, permeability, loss tangent, Q-factor, dielectric constant and AC resistivity of the samples. Curie temperature (T_c), the real part of initial permeability (µ´), loss tangent (tan ?), and AC resistivity have been found to be decreased while the Q-factor increases with the increase in Ca-content. The frequency characteristics of the dielectric constant and AC resistivity have been found to be decreased as the frequency increases. Maxwell-Wagner interfacial type of dielectric polarization was observed with the addition of Ca-content over the entire range of frequency considered.

Keywords: Spinel ferrites; Sintering temperature; Initial permeability; Dielectric constant.

© 2012 JSR Publications. ISSN: 2070-0237 (Print); 2070-0245 (Online). All rights reserved.

doi: http://dx.doi.org/10.3329/jsr.v4i2.9752 J. Sci. Res. 4 (2), 297-306 (2012)