Transport And Magnetic Properties Of (Fe<sub>100-x</sub>V<sub>x</sub>)<sub>75</sub> P<sub>15</sub>C<sub>10</sub> Amorphous Alloys

Authors

  • MAS Karal Department of Physics, Bangladesh University of Engineering and Technology (BUET), Dhaka
  • M Kamruzzaman Department of Physics, Bangladesh University of Engineering and Technology (BUET), Dhaka
  • FA Khan Department of Physics, Bangladesh University of Engineering and Technology (BUET), Dhaka

DOI:

https://doi.org/10.3329/jbas.v35i2.9420

Keywords:

Resistivity, Mooij correlation, Hall resistivity, Magnetoresistance, Saturation magnetization

Abstract

(Fe100-xVx)75 P15C10 (x = 0, 5, 10 and 15) amorphous alloys in the form of ribbon were prepared by the standard melt spinning technique and studied their transport and magnetic properties. The resistivity follows ‘Mooij correlation’ at low temperature (300 - 93) K. The Hall resistivity and the magnetoresistance (MR) were measured in an applied magnetic field up to 0.6T at room temperature (RT = 300 K). Anomalous Hall effect was observed in the Hall resistivity measurement and MR was found to vary 0 - 8%. The saturation magnetization gradually decreased with the increase of V in the alloys at RT.

Key words: Resistivity; Mooij correlation; Hall resistivity; Magnetoresistance; Saturation magnetization

DOI: http://dx.doi.org/10.3329/jbas.v35i2.9420

JBAS 2011; 35(2): 161-169

Downloads

Download data is not yet available.
Abstract
163
PDF
134

Downloads

How to Cite

Karal, M., Kamruzzaman, M., & Khan, F. (2012). Transport And Magnetic Properties Of (Fe<sub>100-x</sub>V<sub>x</sub>)<sub>75</sub> P<sub>15</sub>C<sub>10</sub> Amorphous Alloys. Journal of Bangladesh Academy of Sciences, 35(2), 161–169. https://doi.org/10.3329/jbas.v35i2.9420

Issue

Vol. 35 No. 2 (2011)

Section

Articles