Effects Of Cd On Physical And Some Magnetic Properties Of Co-Cd Ferrites

Authors

  • Saroaut Noor Department of Physics, Khulna University of Engineering and Technology, Khulna
  • SS Sikder Department of Physics, Khulna University of Engineering and Technology, Khulna
  • M Samir Ullah Department of Physics, Bangladesh University of Engineering and Technology
  • MA Hakim Materials Science Division, Atomic Energy Centre, Dhaka
  • Shireen Akhter Materials Science Division, Atomic Energy Centre, Dhaka

DOI:

https://doi.org/10.3329/jbas.v35i2.9429

Keywords:

Co-Cd ferrite, Lattice parameter, Permeability

Abstract

Polycrystalline samples of Cd substituted cobalt ferrites with composition Co1-xCdxFe2O4 (x = 0.0- 0.6 in steps of 0.1) were prepared by double sintering ceramic method. The samples were sintered at 1050°C for 3 hours. X-ray diffraction pattern of the samples showed single phase cubic spinel structure. It was found that the lattice parameter increases linearly with increasing Cd content following Vegard’s law. The apparent density and X-ray density exhibited similar behavior. The Curie temperature Tc has been determined from the temperature dependence of permeability. It was found that the Curie temperature continuously decreased with increasing Cd content and is attributed to the weakening of JAB exchange interaction. The initial permeability, μ' increases with increasing Cd content up to x = 0.6 and then decreases.

Key words: Co-Cd ferrite; Lattice parameter; Permeability

DOI: http://dx.doi.org/10.3329/jbas.v35i2.9429

JBAS 2011; 35(2): 229-235

Downloads

Download data is not yet available.
Abstract
102
PDF
120

Downloads

How to Cite

Noor, S., Sikder, S., Ullah, M. S., Hakim, M., & Akhter, S. (2012). Effects Of Cd On Physical And Some Magnetic Properties Of Co-Cd Ferrites. Journal of Bangladesh Academy of Sciences, 35(2), 229–235. https://doi.org/10.3329/jbas.v35i2.9429

Issue

Vol. 35 No. 2 (2011)

Section

Articles